Sulfur dioxide test with condensation of moisture (Kesternich test) of coated and non coated steels

Presentation for participants

Reference of the ILC	HS-X-FS
References of test methods	ISO 22479 ISO 6988 ISO 3231 ASTM G87 ISO 2808 ASTM B659 ASTM D1186 ISO 2813 ASTM D523 ISO 7724 Parts 1, 2 & 3 ISO 11664 Parts 1 & 4 ASTM E308 ISO 2409 ASTM D3359 Met. B ISO 10289 ISO 4628 Parts 1 to 8 ASTM D610 ASTM D714 ASTM D1654
References of test methods for which the ILC can indirectly provide an assessment of performance	ISO 17872
	These may be superseded standards, which some of the reference standards may have replaced, or EN or ASTM or ISO standards that are close but not exactly equivalent to the reference standards.

Frequency	For this ILC, there is a risk that the number of registrations is low. To ensure an enough number participants, a pre-registration procedure is put in place, as follows:
	1 - Participants interested in participating pre-register using the registration form. No invoicing is made for this pre-registration;
	2 - When at least 10 potential participants have pre-registered, CompaLab asks each of these pre-registrees to confirm their willingness to participate and what are the characteristics for which they commit to provide results;
	3 - If at least 8 participants confirm their intention to participate, the CIL organisation concerned is engaged.
Main characteristics	Loss of mass in a fixed exposure time, before and after removing the corrosion products. Selected exposure times: 7x24h (non coated samples) and 28x24h (coated samples).
Other characteristics	A (against ISO 10289), Percentage of corroded surface (zinc coated sample) - Rating of defects due to ageing in accordance with ISO 4628-2, -3 and -8 - Cross-test against ISO 2409 (paint coated sample)
	Caution The number of determinations may be low for the secundary characteristics, what may make inefficient the comparison between laboratories

Format of the test results:	Results of some properties are numerical and some are expressed as a choice between several possibilities (categories).

Determination of the assigned values (“true values” for each characteristic)	By statistical computation of the totality of the results with possible selection on competence criteria (accreditation, validation by a reference body, quantity of tests performed in the year), test to detect possible collusion, merging of results not obtained in reproductibility conditions, suppression of technically unvalid results.
Type of statistical computation	For numerical results, the statistical computation will provide an assigned value with its attached uncertainty, values of standard deviations for repeatability and reproductibility, limits of alerts for bias and repeatability of the participant, indiviual values for uncertainty of results of participants.
	For results expressed as a choice between several possibilities (categories), Gower indexes are computed from the results, which enables the calculation of assigned values, repeatability and reproducibility standard deviations, limits of alerts for bias and repeatability of the participant, indiviual values for uncertainty of results of participants.
Number of products submitted to tests	3
Number of samples per participation	6
Max number of operators per participation	1 (it is necessary to order as many participations as there are participating test operators)
Product submitted to tests	For this ILC, 3 different products (uncoated steel, galvanised steel, painted steel) are provided for testing.
Type of samples	Plates
Approximate dimensions of samples	150x100x1 mm
Specific preparation to be performed by the participant	Protection of edges

Special notice for this ILC	3 series of samples are provided: one series of uncoated samples (exposure 48h), one series of zinc coated samples (exposure 28x24h), one series of paint coated samples with a scribe against ISO 17872 (exposure 28x24h)

Price (€)		375
Price if online payment (€)		300
Approximate weight (kg)		3